Efeito da termorretificação nas propriedades tecnológicas do bambu

Show simple item record

dc.contributor.advisor Paes, Juarez Benigno
dc.contributor.author Brito, Flávia Maria Silva
dc.date.accessioned 2013-09-26T19:53:45Z
dc.date.available 2013-09-26T19:53:45Z
dc.date.issued 2013-02-26
dc.identifier.citation BRITO, F.M.S. Efeito da termorretificação nas propriedades tecnológicas do bambu . 2013. 99 f. Dissertação (Mestrado em Ciências Florestais) - Universidade Federal do Espírito Santo, Jerônimo Monteiro. 2013. pt_BR
dc.identifier.uri http://www.bibliotecaflorestal.ufv.br/handle/123456789/4096
dc.description Dissertação de Mestrado defendida na Universidade Federal do Espírito Santo pt_BR
dc.description.abstract Este trabalho teve como objetivos avaliar as características anatômicas e físicas do bambu “in natura”, analisar os efeitos da termorretificação nas propriedades tecnológicas do bambu laminado colado termorretificado (BLCTR) e na sua durabilidade natural. Foram coletados quatro colmos em idade adulta e cortados a cada 2,0 m, divididos em quatro secções no sentido longitudinal sendo imersas em água durante 10 dias e secas ao ar. As secções foram transformadas em taliscas com dimensões de 0,5 x 3,5 x 45 cm (espessura x largura x comprimento) e tratadas termicamente a 100, 140, 160, 180 e 200° durante uma hora para cada C, temperatura. Os adesivos utilizados foram o “Cascophen RS-216-M”, à base de resorcinol - formaldeído, “Cascamite PL-2030”, à base de uréia - formaldeído, ambos termofixos e um termoplástico à base de acetato de polivinila, “Cascorez 2500”. As taliscas termorretificadas foram dimensionadas conforme cada ensaio realizado. Observou-se que os colmos de bambu possuem uma frequência de vasos de 0 a 4 vasos.mm-2 com média de 2 vasos.mm-2, fibras longas e estreitas com comprimento médio de 2,72 mm. A massa específica básica de 0,66 g.cm-3 e a retratibilidade volumétrica de 15,41%. Os teores de extrativos e lignina total aumentaram, conforme o incremento da temperatura, e o teor de holocelulose foi reduzido. A partir da temperatura de 160 ° ocorreu um ganho na durabilidade C natural do bambu e na estabilidade dimensional do BLCTR aderido com RF, porém houve uma queda nos valores da massa específica básica e na resistência mecânica do material. pt_BR
dc.description.abstract This work aimed to evaluate the physical and anatomical characteristics of bamboo "in natura", analysing the effects of thermal treatment on the technological properties of glued laminated bamboo thermo-modified (GLBT) and in your natural durability. A total of four culms were collected in age adulthood and cut every to 2.0 m and divided into four lengthwise sections that were immersed in water for 10 days and air-dried. The sections were transformed into flights with dimensions of 0.5 x 3,5 x 45 cm (thickness x width x length) and thermal treated to 100, 140, 160, 180 and 200 ° for one hour for each temperature. T he adhesives used were C “Cascophen RS-216-M”, based resorcinol – formaldehyde, “Cascamite PL-2030”, based on urea - formaldehyde, both thermoset and thermoplastic based on one polyvinylacetate, “Cascorez 2500”. The flights thermal treated were scaled according to each proposed test. It was observed that the bamboo culms have a frequency of 0 to 4 vessels.mm-2, whith mean of vessels.mm-2, with long and narrow fibres with length average of 2.72 mm. The basic specific gravity was of 0.66 g.cm-3 and volumetric shrinkage of 15.41%. The total extractives and lignin contents increased as the temperature increase, and holocellulose content has been reduced. Since the temperature of 160 ° was a gain in durability natural C bamboo and the dimensional stability of GLBT adhered to RF, but there was a decrease in the values of specific gravity and mechanical properties of the material. pt_BR
dc.format 99 folhas pt_BR
dc.language.iso pt_BR pt_BR
dc.publisher Universidade Federal do Espírito Santo pt_BR
dc.title Efeito da termorretificação nas propriedades tecnológicas do bambu pt_BR
dc.title Effect of the thermal treatment in the technological properties of the bamboo pt_BR
dc.type Dissertação pt_BR

Files in this item

Files Size Format View Description
dissertacao_Flavia Maria Silva Brito.pdf 1.958Mb application/pdf View/Open ou Pre-visualizar Tese

This item appears in the following Collection(s)

Show simple item record

Search DSpace


Sobre a Biblioteca Florestal

Browse

My Account