Evaluation of Melamine-Modified Urea-Formaldehyde resin for plywood flooring adhesive application

Show simple item record

dc.contributor.author Oh, Yong-Sung
dc.contributor.author Kim, Kyung-Hee
dc.date.accessioned 2015-11-10T13:02:27Z
dc.date.available 2015-11-10T13:02:27Z
dc.date.issued 2011-06
dc.identifier.citation OH, Y. S.; KIM, K. H. Evaluation of Melamine-Modified Urea-Formaldehyde resin for plywood flooring adhesive application. Scientia Forestalis, Piracicaba, v. 39, n. 90, p. 199-203, jun. 2011. pt_BR
dc.identifier.issn 2318-1222
dc.identifier.uri http://www.bibliotecaflorestal.ufv.br:80/handle/123456789/16183
dc.description.abstract Uma resina de uréia-formaldeído modificada por melamina (MUF) como adesivo de madeira compensada para assoalho, foi sintetizada em laboratório com uma relação molar de 1,48 de formaldeído/(uréia + melamina). As características físicas da resina MUF incluindo sólidos não voláteis, peso específico, pH, formaldeído livre e viscosidade, etc., foram determinadas. A resina MUF foi aumentada com farinha de cones de pinheiro e NH4Cl. A mistura continha aproximadamente 39% de sólidos de resina, 55,8% de sólidos totais e 44,2% de água. O tempo de mistura gel com o catalisador foi de 1,9 minutos a 100 ºC. Foram feitos painéis de compensado em laboratório com o adesivo, usando-se madeiras coreanas. Os painéis de compensado foram testados para tensão de cisalhamento depois de submersos em água a 60 ºC como método de envelhecimento, também para o módulo de ruptura, emissão de formaldeído e abrasão de superfície de acordo com os procedimentos KS F 3101 e KS F 3114. O resultado do teste mostrou que era possível usar a resina MUF para a aplicaçã da produção de compensado para assoalho Ondol. pt_BR
dc.description.abstract A melamine-modified urea-formaldehyde (MUF) resin, as a plywood flooring adhesive, was synthesized in the laboratory with a formaldehyde/(urea + melamine) mole ratio of 1.48. The physical characteristics of the MUF resin including nonvolatile solids, specific gravity, pH, free formaldehyde, and viscosity, etc., were determined. The MUF resin was mixed with an extender, pinenut flour and NH4Cl. The mixture contained approximately 39 percent resin solids, 55.8 percent total solids, and 44.2 percent water. The mixture gel time with the catalyst was 1.9 minutes at 100ºC. Laboratory plywood panels with the MUF resin adhesive mixture were made using Korean wood species. The plywood panels were tested for tension shear strength after 3-hour soak (60ºC water) aging method, modulus of rupture, formaldehyde emission, and surface abrasion according to the procedures of KS F 3101, and KS F 3114. The test results showed that the MUF resin can be used for Ondol plywood flooring production. pt_BR
dc.format 5 páginas pt_BR
dc.language.iso pt_BR pt_BR
dc.publisher Instituto de Pesquisas e Estudos Florestais pt_BR
dc.relation.ispartofseries Scientia Forestalis:v.39,n.90;
dc.subject.classification Ciências Florestais::Tecnologia e utilização de produtos florestais::Tecnologia de produtos florestais não madeireiros pt_BR
dc.title Evaluation of Melamine-Modified Urea-Formaldehyde resin for plywood flooring adhesive application pt_BR
dc.title Avaliação da resina da Uréia-Formaldeido Modificada por Melamina para aplicação como aderente de madeira compensada em assoalho pt_BR
dc.type Artigo pt_BR

Files in this item

Files Size Format View
Scientia_Forestalis_v39_n90_p199-203_2011.pdf 367.2Kb application/pdf View/Open ou Pre-visualizar

This item appears in the following Collection(s)

Show simple item record

Search DSpace


Sobre a Biblioteca Florestal

Browse

My Account