2024-03-29T13:18:54ZUtilização de resíduos da madeira de candeia (Eremanthus erythropappus (DC.) Macleish) na produção de painéis aglomerados com adição de pet
http://hdl.handle.net/123456789/10402
Utilização de resíduos da madeira de candeia (Eremanthus erythropappus (DC.) Macleish) na produção de painéis aglomerados com adição de pet; Utilization of candeia (Eremanthus erythropappus (DC.) Macleish) wood residues in the production of particleboad with addition of pet
Santos, Rosimeire Cavalcante dos; Mendes, Lourival Marin; Carneiro, Angélica de Cássia Oliveira; Mori, Fábio Akira; Castro, Renato Vinícius Oliveira; Mendes, Rafael Farinassi
Este trabalho objetivou analisar, por meio das propriedades físicas e mecânicas, a viabilidade da produção
de painéis a partir da incorporação do resíduo da madeira de candeia (Eremanthus erythropappus) e a
influência das diferentes porcentagens de plástico tipo PET (polietileno tereftalato), como também da
presença e ausência de parafina sobre as propriedades dos painéis aglomerados. Foram utilizados resíduos
da madeira de candeia, após a extração do óleo, em associação à madeira de eucalipto, na proporção de
25:75, e adesivo uréia-formaldeído (12%) para a produção dos painéis; além da incorporação de PET na
forma de partículas originadas de envases de refrigerantes em três porcentagens de incorporação (0%,
25% e 50%) em tratamentos na presença (1%) e ausência de emulsão de parafina. O ciclo de prensagem
dos painéis ocorreu sob aquecimento elétrico a temperatura de 160oC; pressão de 0,4MPa e tempo de 8
minutos. O experimento foi instalado em um delineamento inteiramente casualizado com três repetições.
As propriedades avaliadas, segundo as normas DIN (1971), ASTM D 1037-93 (1995) e CS 236-66 (1968),
foram: ligação interna; flexão estática (módulo de elasticidade - MOE e módulo de ruptura - MOR);
compressão paralela à superfície das chapas; absorção de água e inchamento em espessura, após 2 e 24
horas de imersão. As propriedades mecânicas dos painéis foram reduzidas com o aumento dos níveis de
incorporações de PET; a adição de parafina não promoveu, de modo geral, ganhos de resistência e redução
de higroscopicidade dos painéis madeira-plástico; é viável a utilização do resíduo da madeira de candeia,
em associação à madeira de eucalipto, na confecção dos painéis madeira-plástico, pois as propriedades
atenderam às exigências mínimas das normas, exceto para o teste de flexão estática.; This work aimed to evaluate, through the physical and mechanical properties, the panels production
viability with inclusion of candeia (Eremanthus erythropappus) wood residues and the influence of different
percentages of PET (polyethylene terephthalate), as well as the presence and absence of paraffin on the
properties of particleboard. There were used candeia wood residues, after oil extraction, in association with
eucalypt wood in the proportion of 25:75 and urea-formaldehyde adhesive (12%) for panels production;
besides the PET incorporation in particle form, which were originated from soft drink bottles and included
in three percentages (0%, 25% e 50%) in treatments in the presence (1%) and absence of paraffin emulsion.
The panels pressing cycle occurred under electric heating at 160°C, 0.4 MPa of pressure, during 8 minutes.
The experimental design was entirely randomized with three repetitions. The properties evaluated, according
to DIN (1971), ASTM D 1037-93 (1995) and CS 236-66 (1968) standards, were: internal bonding; static
bending (modulus of elasticity – MOE and rupture – MOR); compression parallel to the panel surface; water
absorption and thickness swelling, after 2 and 24 hours water soaking. The panel mechanical properties
decreased with increasing in PET level; in general, paraffin addition did not improve the wood/plastic
panels resistance and higroscopicity; the utilization of candeia wood residues is viable, in association with
eucalypt wood, for the wood/plastic panel production, since the properties attended the minimum demands
of the standards, except static bending.
2011-01-01T00:00:00ZProdução do Pinus taeda L. em povoamento desbastado na região dos Campos de Cima da Serra, Rio Grande do Sul
http://hdl.handle.net/123456789/10401
Produção do Pinus taeda L. em povoamento desbastado na região dos Campos de Cima da Serra, Rio Grande do Sul; Yield of Pinus taeda L. in thinned stand in the Campos de Cima da Serra region, Rio Grande do Sul
Elesbão, Luiz Ernesto Grillo; Schneider, Paulo Renato
Este trabalho foi realizado com o objetivo de estudar a produção do Pinus taeda L., implantado num
espaçamento inicial de 3 x 2 m, localizado em Canela, estado do Rio Grande do Sul. A população amostral
foi submetida a um e dois desbastes seletivos, além da manutenção de uma testemunha, sem desbaste. Os
desbastes foram realizados por baixo com redução da área basal para níveis de 28 m2ha-1. Aos 17 anos, a
produção total das parcelas testemunhas, sem desbaste, foi de 886,3 m3ha-1; com a realização de um desbaste
aos 11 anos, de 756,6 m3ha-1, tendo resultado perdas de produção em relação a testemunha de 14,6 %; com
dois desbastes aos 11 e 15 anos, a produção foi de 732,9 m3ha-1, tendo provocado perdas de produção em
relação à testemunha, sem desbaste, de 17,3 %. Os desbastes executados permitiram um ganho significativo
em diâmetro, até os 17 anos de idade, com a execução de um desbaste aos 11 anos obteve-se um diâmetro
médio de 33,4 cm; com dois desbastes aos 11 e 15 anos, um diâmetro médio de 33,5 cm; e, um diâmetro
médio de 24,3 cm na testemunha, sem desbaste.; This work was carried out with the objective of studying the yield of Pinus taeda L., planted in an initial
spacing of 3 x 2 m, located in Canela, Rio Grande do Sul state. The amostral population was submitted
to one and two selective thinning, beyond a control sample, without thinning. The selective low thinning
was conducted with reduction of the basal area to levels of 28 m2/ha. At age 17, the total yield of the
control sample, without thinning, was 886.3 m3ha-1; with one thinning at age 11 the yield was 756.6 m3ha-
1
, resulting in losses of yield of 14.6% compared to the control; with two selective at ages 11 and 15, the
yield was 732.9 m3ha-1, resulting in losses of yield in relation with the control sample, without thinning, of
17.3%. The selective thinning allowed a significant gain in diameter, up to age 17; with the execution of a
selective thinning at age 11 an average diameter of 33.4 cm; was obtained with two selective thinning at
ages 11 and 15 an average diameter of 33.5 cm; and an average diameter of 24.3 cm in the control sample,
without thinning.
2011-01-01T00:00:00ZComportamento de Peltophorum dubium (Spreng.) Taub., Parapiptadenia rigida (Benth.) Brenan e Enterolobium contortisiliquum (Vell.) Morong cultivadas em solo contaminado com cobre
http://hdl.handle.net/123456789/10393
Comportamento de Peltophorum dubium (Spreng.) Taub., Parapiptadenia rigida (Benth.) Brenan e Enterolobium contortisiliquum (Vell.) Morong cultivadas em solo contaminado com cobre; Performance of Peltophorum dubium (Spreng.) Taub., Parapiptadenia rigida (Benth.) Brenan and Enterolobium contortisiliquum (Vell.) Morong cultivated in copper contaminated soil
Silva, Rodrigo Ferreira da; Lupatini, Manoeli; Antoniolli, Zaida Inês; Leal, Lineu Trindade; Moro Junior, Carlos Augusto
Solos contaminados por cobre podem interferir no desenvolvimento fisiológico e no estabelecimento de
plantas. Uma opção para revegetação desses solos é a utilização de espécies florestais nativas tolerantes ao
cobre. Este trabalho teve como objetivo avaliar a tolerância de três espécies florestais nativas ao excesso
de cobre no solo. As espécies utilizadas foram: angico – Parapiptadenia rigida, canafístula – Peltophorum
dubium e timbaúva – Enterolobium contortisiliquum. O delineamento experimental foi inteiramente
casualizado, num esquema 3 x 5, sendo três espécies florestais e cinco doses de cobre (0, 64, 128, 192 e
256 mg kg-1 de solo), com seis repetições. Determinou-se a altura de planta, massa seca da parte aérea,
comprimento e área superficial específica radicular, teor de cobre na parte aérea e na raiz. A timbaúva e a
canafístula apresentam tendência de armazenamento do cobre nas raízes e baixa translocação para a parte
aérea. A massa seca da parte aérea da timbaúva e canafístula é incrementada com pequenas doses de cobre,
enquanto que a massa seca da parte aérea do angico não é afetada pelas doses testadas. A timbaúva e o
angico demonstram maior capacidade de tolerância à contaminação de cobre no solo que a canafístula.; Soils contaminated by copper may interfere with the physiological development and establishment of
plants. An alternative for the revegetation of these soils is the use of native species tolerant to copper. This
study aimed to evaluate the tolerance of three native forest species to excess copper in the soil. The species
used were: angico - Parapiptadenia rigida, canafistula - Peltophorum dubium and timbauva - Enterolobium
contortisiliquum. The experiment was completely randomized in a 3 x 5 schedule, with three tree species
and five doses of copper (0, 64, 128, 192 and 256 mg kg-1 soil) with six replicates. Plant height, shoot
dry weight, length and specific root surface area and copper content in shoots and roots were determined.
Canafistula and timbauva species showed storage of copper in roots and low translocation to the shoot.
The shoot dry weight of timbauva and canafistula increased with small doses of copper while the shoot dry
mass of angico was not affected by the doses tested. The timbauva and angico showed greater capacity for
tolerance to copper contamination in the soil than did canafistula.
2011-01-01T00:00:00ZModelos de índice de sítio para o pinheiro calabrês (Pinus brutia Ten.) na ilha Thasos, Grécia
http://hdl.handle.net/123456789/10392
Modelos de índice de sítio para o pinheiro calabrês (Pinus brutia Ten.) na ilha Thasos, Grécia; Site index models for calabrian pine (Pinus brutia Ten.) in Thasos island, Greece
Kitikidou, Kyriaki; Bountis, Diamantis; Milios, Elias
Um modelo de índice de sítio para o pinheiro calabrês (Pinus brutia Ten.) na ilha Thasos Grécia foi
apresentado. O modelo foi ajustado e validado com dados de análises de tronco de 150 árvores, obtidas de
75 parcelas de área fixa provenientes de cinco sítios experimentais. Quatro equações de crescimento em
altura na forma de diferença algébrica foram testadas, sendo que a função de BAILEY e CLUTTER (1974)
foi considerada apropriada devido à sua boa performance tanto com dados de ajuste como os de validação.
Os resultados mostraram erros mais baixos do que 5 % e pouco viés.; A site index model for Calabrian pine (Pinus brutia Ten.) in Thasos island (North Aegean sea, Greece) is presented. The model was fitted and validated from 150 stem analyses, obtained from 75 fixed-area plots from five experimental sites. Four height growth equations of difference form were tested and the BAILEY and CLUTTER (1974) function was considered appropriate due to its good performance with both fitting and validation data. The results show errors lower than 5% and little bias.
2011-01-01T00:00:00Z